ISONEM LIQUID GLASS is a two-component product which excellently adheres to surface like glass, mosaic, tile, porcelain, ceramic, marble, granite, natural stone, wood, concrete, screed, galvanized sheet, aluminum etc.. The product which has a high resistance to atmospheric conditions can be used for waterproofing and decorative purposes. Produced in transparent the product has high chemical and physical besides excellent water resistance. It is not affected by U.V and outdoor weather conditions. It does not get yellow, fading or peeling off in time. It is especially applied as a solution to insulation problems arising on the floors such as balconies, terraces, bathrooms easily and without damaging the existing coating.
Density A comp. (25°C, g/mL) : 0,90 ± 0,10
Density B comp. (25°C, g/mL) : 0,95 ± 0,10
pH (25°C) : Not applicable (N/A)
Viscosity B comp. (25°C, mPa.s) : 0 – 500
Solid content B comp. (% Weight) : Not applicable (N/A)
Water transmission rate (kg/ m2. h0,5) : < 0,1 CLASS W3
Adhesion strength by pull-off test (N/mm2) : Rigid system without trafficking ≥ 1.0 N/mm²
Permeability to water vapour (m) : 5 ≤ SD ≤ 50 CLASS II
Surface preparation: The relative humidity of the air should be maximum 80%, the ambient temperature should be 15 – 35 ° C and the surface temperature to be applied should be at least 5 ° C. It should not be applied in rainy weather. For good adhesion, surface cleaning should be done very well. Any kind of oil, dust, dirt, rust and similar substances on the surfaces to be applied between the liquid glass and the floor which may prevent the liquid glass from sticking to the surface should be completely cleaned. In tile, ceramic applications, if existing joint fillings were worn away, they should be renewed. The sanded surface provides better mechanical properties for liquid glass application and helps to better adhesion of the liquid glass to the surface.
Application method: Before application, the two components must be mixed thoroughly and at the given ratios. The two components can react only when the mixture is uniform and complete. The number of floors to be applied for the best performance is indicated in the table below.